Field of Science: Statybos inžinerija / Civil engineering (T002)
Author(s): Vaičiukynienė, Danutė;Vaitkevičius, Vitoldas;Rudžionis, Žymantas;Vaičiukynas, Vilimantas;Navickas, Arūnas Aleksandras;Nizevičienė, Dalia
Title: Blended cement systems with zeolitized silica fume
Is part of: Materials science = Medžiagotyra / Kaunas University of Technology, Academy of Sciences of Lithuania. Kaunas : KTU, 2016, Vol. 22, no. 2
Extent: p. 299-304
Date: 2016
Keywords: Zeolitized silica fume;Cement hydration;Hydrosodalite
Abstract: In this paper the properties and the hydration of Portland cement pastes containing zeolitized silica fume were studied. Hydrosodalite was obtained by zeolitization of silica fume. XRD, DSC, SEM and energy-dispersive X-ray spectroscopy were used as investigation methods. The compressive strength of hardened cement paste was measured after 28 days. The levels of cement replacement by additives were 5 %, 10 % and 15 % by weight in the specimens. Changes in the strength of hardened cement paste were observed. The influence of additives on hydration rate and hydration temperature was also observed. Both 1Hs (hydrosodalite) and 2Hs (modified hydrosodalite) additives accelerate the hydration of the cement paste. The highest hydration temperature was achieved in a mixture with 5 wt. % 1Hs additive and with 10 wt. % 2Hs additive. The microstructure of hardened cement paste specimens with 1Hs and 2Hs additive is denser compared with reference specimens without the additives. The maximum compressive strength of the specimens with 10 wt. % of 2Hs reached up to 101 MPa under laboratory conditions
Internet: http://matsc.ktu.lt/index.php/MatSc/article/view/7018/7753
Affiliation(s): Kauno technologijos universitetas
Vytauto Didžiojo universitetas
Žemės ūkio akademija
Appears in Collections:Universiteto mokslo publikacijos / University Research Publications

Files in This Item:
marc.xml7.23 kBXMLView/Open

MARC21 XML metadata

Show full item record
Export via OAI-PMH Interface in XML Formats
Export to Other Non-XML Formats


CORE Recommender

WEB OF SCIENCETM
Citations 5

5
checked on Jan 17, 2021

Page view(s)

52
checked on Jan 7, 2020

Download(s)

6
checked on Jan 7, 2020

Google ScholarTM

Check

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.